Curing of positive plates. This is the most time consuming technological procedure (24-72 hours). During curing the following processes take place: Pb oxidation; recrystallization of 3BS, 4BS and PbO; grid corrosion; improvement of the paste/grid contact, and drying of the paste. With increase of curing temperature the rates of the curing processes will be accelerated and curing time can be shortened. At to > 65oC, 3BS paste transforms into 4BS paste comprising large crystals which are difficult to oxidize to PbO2 during formation. With the new technology for paste preparation from 4BS+Pb3O4 the upper temperature limit of curing is eliminated. The processes during curing of 4BS+Pb3O4 paste at 93oC with H2O vapour purged through the curing chamber have been investigated. It has been established that curing of 4BS pastes under these conditions proceeds for less than 8 hours. Batteries manufactured with such plates have initial capacity equal to the rated one and cycle life considerably longer than that of batteries produced from 3BS pastes.
When curing is conducted at temperatures above 80oC, the 3BS particles are converted into 4BS ones which contain water. It has been established that positive plates produced with 4BS pastes cured at 50oC have the longest cycle life and adequate capacity performance. Positive plates prepared with 3BS pastes, which are then converted to 4BS ones during plate curing at 90oC, have high initial capacity and power performance but shorter cycle life. Batteries with plates produced with 4BS and then cured at 90oC for less than 4 h have both satisfactory power output and cycle life.
Curing of negative plates. For high tech battery manufacture the duration of curing of negative plates should be less than 8 hours. Additive B-88 (0.5%) to the negative paste increases the rate of the curing processes at 60oC and shortens the technological procedure of curing to 8 hours. Expanders disintegrate at temperatures higher than 65oC. The new curing mode proposed results in 10% increase in total pore volume of cured paste and 20% increase in dry paste specific surface area, and formation of a fine-grain and more uniform structure.
References
- D. Pavlov, N. Kapkov, High-Temperature Curing of Lead Acid Battery Positive Plates, J. Electrochem. Soc., 137 (1990) 21
- S. Ruevski, D. Pavlov, Accelerated Curing of Negative Plates for Lead/Acid Batteries, J. Power Sources, 31 (1990) 217
- D. Pavlov, M. Dimitrov, T. Rogachev. L. Bogdanova,Influence of the curing conditions on PbCaSn grid/paste interface and lead-acid battery performance, Proceedings of International Conference LABAT’02, Varna, 10-13 June 2002, p.79
- D. Pavlov, M. Dimitrov, T. Rogachev, L. Bogdanova, Influence of paste composition and curing program used for the production of positive plates with PbSnCa grids on the performance of lead acid batteries, J. Power Sources, 114 (2003) 137
Keywords: processes during curing, curing of positive plates, 3BS pastes, 4BS pastes, converting 3BS paste into 4BS, curing of negative plates |